Thyme Functionalized Polydopamine Coated ZnO Nanoparticles With Enhanced Antibacterial Activity For Biomedical Application

Abstract

Bacterial infections are a major cause of injury-related death, and several efforts have been developed to deal this problem. For this goal, we were synthetized a novel antibacterial agent based on thyme functionalized polydopamine coated ZnO NPs ([email protected]). Following the synthesis of ZnO NPs, a one-step, simple method was used to surface modification of[email protected]with TH. The finding proved that creating NPs with a rod-shaped morphology created a large surface area for bacteria to contact. The formation of a homogeneous TH layer on the surface of NPs had no substantial effect on their shape. Antibacterial assays revealed that[email protected]had a much higher antibacterial activity against S. aureus and E. coli. This shows that[email protected]and the TH grafted on the surface of[email protected]have an excellent synergistic antibacterial effect. In conclusion, we suggest that the prepared[email protected]could be useful as antibacterial agents for biomedical uses.

Abstract

Bacterial infections are a major cause of injury-related death, and several efforts have been developed to deal this problem. For this goal, we were synthetized a novel antibacterial agent based on thyme functionalized polydopamine coated ZnO NPs ([email protected]). Following the synthesis of ZnO NPs, a one-step, simple method was used to surface modification of[email protected]with TH. The finding proved that creating NPs with a rod-shaped morphology created a large surface area for bacteria to contact. The formation of a homogeneous TH layer on the surface of NPs had no substantial effect on their shape. Antibacterial assays revealed that[email protected]had a much higher antibacterial activity against S. aureus and E. coli. This shows that[email protected]and the TH grafted on the surface of[email protected]have an excellent synergistic antibacterial effect. In conclusion, we suggest that the prepared[email protected]could be useful as antibacterial agents for biomedical uses.

Keywords

ZnO nanoparticles; Polydopamine; Thyme; Antibacterial agent

Introduction

Bacterial infections are one of the most important problems that extend the various diseases [1-4]。Although the use of antibiotics is a common means to stop bacterial activity, the increasing drug resistance is the major drawback of over prescribing and misuse of antibiotic [5-7]。Therefore, the presence of antimicrobial agents has been illustrated as an alternative approach to locally inhibit bacterial activity without side effects. Antibacterial Nanoparticles (NPs) are one of the promising agents that can limit bacterial activity [8,9]。Nanotechnology has developed various types of nanoscale materials [10]。NPs are a broad class of materials that include particulate substances that have at least one dimension of less than 100 nm [11]。许多不同类型的金属NPs黄金等(Au), silver (Ag), zinc (Zn), and copper (Cu) play an important role in nanoscience and have many interesting applications, including interesting biomedical and optical uses due to their inherent antibacterial activity and brilliant colors [12]。As we know, inorganic antibacterial agents have great migration resistance, such as Ag, ZnO and Titanium Dioxide (TiO2) NPs [13,14]。Ag NPs is the typical representative of inorganic antibacterial agents with excellent antibacterial activity [15,16]。However, its safety is controversial. Some studies indicate that Ag is toxic to the humans and environment [17]。Besides, polymer composites with Ag experience color changes owing to the Ag discoloration, which severely limits its potential uses. In addition, Ag material is costly and the Ag NPs synthesis process is complicated. ZnO is another antibacterial agent that has attracted much interest due to its low cost, high temperature resistance, antibacterial activity, photocatalysis and UV protection, color change at high temperatures, and most importantly, its safety to humans [18-20]。It is detected as a biologically safe inorganic material. Its application in cosmetic products is approved by the FDA (Food and Drug Administration) [21]。然而,氧化锌的缺点是它的一个tibacterial activity is too low. Therefore, after the ZnO antibacterial activity is increased, a type of excellent antibacterial agent with excellent antibacterial activity, safety, and high temperature resistance can be acquired [22]。

Surface modification of NPs with different kinds of functional groups and surface coatings are promising approaches to omit several inorganic NPs drawbacks for biomedical uses [23]。Moreover, the coatings can interact with complex biological environments and exhibit different properties depending on the application. Considering the safety and the excellent antibacterial efficacy of natural organic antibacterial agents, they are very appropriate for NPs modification to improve antibacterial activity, such as Thyme (TH) [24,25]。TH is a safe and harmless natural antibacterial and biocidal monoterpenoid agent derived from the thymus gland. It also has proper antibacterial activity against bacteria, fungi, yeast, and mold[26,27]。TH is generally recognized as a safe food additive according to the FDA [28]。Moreover, the other characteristics of TH are antifungal, antioxidant, antidiabetic, anti-inflammatory and also antitumoral alone or in combination with other compounds. In this regard, TH and Cinnamaldehyde (CA) were used in a study to modify ZnO. The antibacterial activity assays showed that TH and CA also had an excellent synergistic effect to improve the antibacterial property of ZnO-TH-CA [29]。The results also suggest that it is an effective approach to achieve a highly effective antibacterial agent by grafting both the hydrophilic TH and hydrophobic CA onto the same surface of ZnO. Dopamine (DOP) is a molecule that can mimic the bioadhesive behavior of mussels and is readily deposited on a variety of substrates by self-polymerization, resulting in Polydopamine (PDA) [30]。Due to the abundant amine and catechol groups on the surface, PDA films reportedly serve as an active template and a good reducing agent to reduce Zn ions to ZnNPs [31,32]。A suitable thickness of PDA film can inhibit Zn migration. In this content, researchers prepared PDA coated ZnO rod-shaped NPs ([email protected]) with significant antibacterial activity and biocompatibility. They showed that the developed[email protected]NPs were not only non-toxic to human cells, but also remarkably promoted cell survival compared to ZnO NPs. The development of reinforced active[email protected]NPs using natural TH has not yet been investigated. This study aimed to prepare a novel system based on ZnO NPs and TH-PDA ([email protected]) and studying the role of TH coating on the ZnNPs antibacterial activity [33-35]。

Material and Methods

ZnO nanoparticles (range of particle size 10-30 nm) were obtained from nanosany corporation Co. Mashhad, Iran. Dopamine hydrochloride 98% was purchased Sigma-Aldrich. Thyme powder was obtained from Tabriz, Iran. Escherichia coli ATCC 25922 and Staphylococcus aureus ATCC 25923 standard strains were obtained from Persian Type Culture Collection (PTCC). All other solvents and reagents were of reagent grade.

Synthesis of polydopamine functionalized ZnO NPs ([email protected])

[email protected]was prepared by adding ZnO NPs to the aquas solution of dopamine [36]。Briefly, 40 mg ZnO nanoparticles was primarily washed and dispersed in deionized water by sonication. A fresh dopamine solution was prepared by dissolving of 10 mg dopamine in Tris-HCl buffer solution (pH=9) with the concentration of 2 mg/ml. Then, ZnO NPs were dispersed into dopamine solution to make a suspension. This suspension was stirred vigorously under 37°C for 24 h. Finally,[email protected]were collected by centrifuging at 10000 rpm for 15 min and freeze-dried.

Synthesis of thyme functionalized Zn/PDA NPs ([email protected])

The thyme solution was prepared by dissolving 100 mg thyme in absolute ethanol.[email protected]was synthesized by the same process as the[email protected]制造。为了这个目的,获得的[email protected]after the centrifuging was dispersed in ethanolic solution of thyme. This suspension was stirred vigorously under 37°C for 24 h and finally was freeze-dried.

Characterization of the synthesized nanoparticles

所有的样品的化学结构evaluated by Fourier transform infrared (FTIR, Bruker, TENSOR 27, Germany) with KBr pellet in the range of 400-4000 cm-1. The morphology of the obtained nanoparticles was observed by scanning electron microscopy (FE-SEM, MIRA3, Tescan). For SEM imaging, firstly, the freeze-dried samples were coated with a thin layer of gold. Also, the Energy Dispersive X-ray spectroscopy (EDX) was used to study the elements of the nanoparticles. The zeta potential of the nanoparticle’s dispersion in deionized water was measured by dynamic light scattering method (ZetaSizer, Malvern Instruments, and Ver. 7.11). X-ray diffraction (XRD. Ital structure, MPD 3000) was used to analyze the structure of the nanoparticles with a 2θ range from 10° to 80° and step size of 0.001.

Antibacterial assays of nanoparticles

The antibacterial activity of the synthesized nanoparticles was assessed againstS. aureus(Gram-positive bacteria) andE. coli(Gram-negative bacteria) based on the Minimum Bactericidal Concentration (MBC) and the Minimum Biofilm Eradication Concentration (MBEC).

Minimum Inhibitory Concentration (MIC) of nanoparticle

microbroth稀释方法用于不同ne the minimum bactericidal concentration of nanoparticles (2019). Serial concentrations of nanoparticles were prepared in MHB (Mueller-Hinton broth) culture media (Merck, Germany). As the concentration of the nanoparticles was adjusted range from 15 to 0.029 mg/ml. A bacterial suspension equivalent to 0.5 McFarland was prepared in sterile normal saline according to the CLSI recommendation (CLSI 2020) and inoculated into the culture medium contains nanoparticle. After 24-hour incubation at 37°C, 100 μl of the test tubes contents were subculture on nutrient agar medium, and the growth of bacterial isolates was investigated. The MBC was defined as the lowest concentration of nanoparticle which kills 99.9% of the test strain. This experiment was conducted separately for three strains.

Minimum Biofilm Eradication Concentration (MBEC)

The Trypticase soy broth (180 μl) containing 0.5% glucose and bacterial suspension (20 μl) equal 0.5 McFarland were added to each well. After incubation overnight at 37 °C, the contents of the wells were removed and washed 3 times with 300 μl of sterile phosphate buffer. Then methanol (150 μl) was added to the wells and was incubated about for 20 min at the lab temperature. For staining, crystal violet (150 μl) was added and at ambient temperature the resultant solution was incubated for 15 min. The plates were washed and thoroughly dried by placing them upside down. Finally, acetic acid 33% (150 μl) was added to the wells and was placed 30 min at ambient temperature. The optical density of the contents of each well was detected by using a microtiter plate reader at 570 nm. According to our previous study, the cut off optical density for biofilm formation was evaluated as follow; strong formation (+++), moderate (++), weakly (+), and No Biofilm formation (0) were recorded. To optimize results and provide reliable data, the experiment was repeated triplicate per strain. Based to the above procedure, the effect of nanoparticles on biofilm eradication was investigated. With the difference that after pouring the culture medium into the wells, serial dilutions of nanoparticles were prepared in each well and bacterial suspension was added to them. Finally, the results were interpreted as follows: no biofilm formation (0); OD ≤ ODc, weak form (+); OD ≤ 2ODc, medium (++); 2ODc

Result and Discussion

As shown inFigure 1, the Novel TH functionalized Zn/PDA NPs ([email protected]) was successfully prepared. The morphology and shape of the obtained NPs were characterized with SEM analysis. The SEM images of the[email protected]and[email protected]showed needle and rod-shaped NPs (Figure 2). This morphology was also detected in similar studies on the ZnO NPs synthesis using Zn(NO₃)₂and Zn(CH3COO)₂precursors. This morphology is favorable for several biomaterials uses due to its large surface-to volume ratio. Antibacterial features of this morphology were also illustrated in a recent study. The[email protected]morphology after coating with thyme was not significantly altered. However, some spherical sedimentation was revealed on the NPs surface, confirming the presence of PDA/TH coating.

The zeta potential is an important factor for studying nanoemulsion stability. In order to find out the prepared NPs surface charge, the Zeta potential test was carried out (Figures 3 a,b). Results showed that the[email protected](−17.2 mV) charge was negatively enhanced compared to[email protected](−8.36 mV). It could be realized that the electrostatic interaction between the amine groups of[email protected]with thyme resulted in the thyme layer formation with hydroxyl functional groups leading to the creation of a negative surface charge.

EDX analysis

The results of the EDX-dot mapping analysis for[email protected]and[email protected]are shown inFigures 4 and 5。The presence of all applied elements, including C, N, O, and Zn, over the surface of the mentioned NPs and also the absence of any impurity were confirmed by EDX assays. The thymol adsorption group over[email protected]was also verified to be responsible for the O signal. Thymol is one of the active chemicals loaded on Zn, therefore the O signal indicates that the[email protected]were perfectly generated via an active, environmentally friendly reduction procedure. The sharp main peak for Zn at ~1 keV is a strong signal for the crystalline nature of biosynthesized NPs and the current work produced a consistent result in line with. Additionally, the peak intensity of each surface element and the value of the existing elements in the sample have proportionate relationships. As a result, the achieved results reveal that the prepared NPs have excellent purities and their compositions are in good accordance with the specified mass percentages, according to this statement. This observation confirms the XRD findings.

FTIR

Figure 6indicates the FTIR spectra of crude TH, ZnO, and modified ZnNPs ([email protected]and[email protected]). The TH spectra (Figure 6a) show an adsorption peak at ~3220 cm-1 corresponding to phenolic -OH stretching involving hydrogen bonding. Aromatic character of TH is indicated by C=C stretching of benzene ring at ~1615 cm-1. The presence of zinc hydroxyl in the composition was demonstrated by the presence of characteristic peaks at ~1425 cm-1 and ~3400 cm-1 in the ZnO spectrum (Figure 6b). Zinc hydroxyl is an intermediate product that cannot be completely removed during the synthesis of ZnO. The spectrum of[email protected]and[email protected]revealed that all of the characteristic peaks, as well as ZnO and TH, were present in the spectra (Figure 2). The[email protected]spectra (Figure 6c) included a peak at 3410 cm-1 corresponding to the stretching vibrations of the O-H and N-H groups in the PDA. Furthermore, the peaks at ~1580 and 1250 cm-1 were related to C=O and C-O bonds, indicating that ZnNPs has been functionalized. The presence of PDA on ZnNPs was also confirmed by the appearance of characteristic peaks corresponding to C=N and C=C groups on the[email protected]spectrum at ~1472 cm-1. The spectrum of TH blended[email protected](Figure 6d) revealed a little shifting of position in the characteristic bands. In[email protected]spectra, the main change was detected for -OH stretching peak (~200 shifts) that might confirm interaction of TH with[email protected]

XRD analysis

The XRD patterns of ZnNPs,[email protected], and[email protected]showed and confirmed the crystalline nature of the NPs (Figure 7). As can be revealed from patterns, the characteristic peaks at around 2θ=31, 34, 36, 47, and 56° related to ZnO crystals [37,38]。In addition, no additional impurity peaks were found in any of the patterns. Owing to the diffraction of the PDA amorphous structure, a broad peak at 2θ=21 emerged alongside ZnO characteristic peaks after ZnO modification with PDA ([email protected]), which is in agreement with the previous report by Tavakoli et al.[35]。In the XRD pattern of[email protected], the remaining peaks of Zn(OH)₂were interestingly erased[39]。It can be concluded that DPA was first incorporated into Zn(OH)₂and ZnNPs with free functional groups of amine and catechol, and oxidized which resulted in the Zn(OH)₂conversion to ZnNPs.

Antimicrobial activity

Table 1reveals the results of study the NPs samples inhibition activity against S. aureus and E. coli strains. The neat TH and[email protected](control) revealed weak inhibition activity against studied bacteria. Nevertheless, the Th incorporated in[email protected]provided greater antibacterial activity. The antimicrobial property of ZnO could be ascribed to the production of Reactive Oxygen Species (ROS) by ZnO, which damages cell wall and disrupts DNA replication and protein synthesis, according to previous literature [40]。Furthermore, the Zn²⁺ions released by ZnO increase the permeability of NPs across the bacteria cell wall, killing bacteria by interacting with cytoplasmic material [41]。The electrostatically or direct interaction between the bacterial surface and ZnO, which resulted in NP penetration in bacterial cells, is another mechanism for ZnO antibacterial activity [42]。The antibacterial activity of NPs againstS. aureuswas shown to be significantly higher than that ofE.coil(seeTables 1 and 2). The bacterial cell wall system plays an important role in bacterial resistance to antibacterial drugs. The peptidoglycan layer of gram-positive bacteria is thicker than that of gram-negative bacteria [43]。However, Gram-negative bacteria have a more complicated cell wall structure, consisting of a thin peptidoglycan layer and an outer membrane with barrier features. As a result, in these bacteria outer membrane layer prevents produced ions and ROS from penetrating the bacterial cell via ZnO NPs.

Table 1.The MBC test at different concentrations (mg/ml) of groups.

Determination of Minimum Bactericidal Concentration (MBC) :The obtained results revealed that the MBC of developed formulations compared with control groups has an excellent effect on bacteria (Table 1).

Assessment of biofilm production by different groups

The bacterial biofilm formation is a defense mechanism that protects them from antimicrobial agents, particularly antibiotics. This characteristic has a significant impact on the clinical outcome ofE. coliandS. aureusinfections. We assessed the production of biofilms in all of the isolates and we find that the strains were strongly positive for biofilm development. Then, in the presence of TH-loaded[email protected],[email protected], and free TH form, the minimal biofilm eradication concentration in these strains was studied. In comparison to control groups, our findings demonstrated that TH-loaded[email protected]can eradicate biofilm formation at low concentrations (Table 2).

Table 2.Assessment of biofilm production by different groups.

Conclusion

In this study we have developed a simple approach for fabricating good antibacterial agents using Thyme (TH) functionalized polydopamine/ZnO NPs ([email protected]). TH was grafted onto the[email protected]successively. The antibacterial activities of the prepared NPs againstS. aureusandE. colibacteria could be notably improved by grafting TH onto the surface of[email protected]due to the good synergistic antibacterial effect of TH and[email protected], according to the results of antibacterial tests. TH grafted onto the[email protected]surface increased TH's contact probability with each bacterium, allowing them to effectively exploit their antibacterial advantages. As a result,[email protected]has a dual synergistic antibacterial effect, enhancing antibacterial activity. Besides, the developed[email protected]supposed a good potential to create blood clotting owing to its negative surface charge. The above observations not only indicated a novel approach for the development of an effective antibacterial agent that was both efficient and environmentally friendly.

Conflicts of Intrerest

There are no conflicts to declare.

Ethics Statement

研究过程是通过by the Ethical Committee of Tabriz University of Medical Science (Approval ID:IR.TBZMED.VCR.REC.1398.303).

Acknowledgements

The authors would like to thank from the “Stem Cell Research Center, Tabriz University of medical sciences” for their kindly cooperation.

References

1. Brachman PS, et al.Bacterial infections of humans: Epidemiology and control。2009.

   [Google scholar]

2. Dadashzadeh K, et al.Real-time PCR detection of 16S rRNA novel mutations associated with Helicobacter pylori Tetracycline resistance in Iran。Asian Pacific J Cancer Prev.2014; 15:8883-8886.

   [Crossref][Google scholar][EBSCO]

3. Coates ARM, et al.Antibiotic combination therapy against resistant bacterial infections: synergy, rejuvenation and resistance reduction。Expert Rev Anti Infect Ther. 2020; 18:5-15.

   [Crossref][Google scholar][EBSCO]。

4. Hendaus MA, et al.Covid-19 induced superimposed bacterial infection。J Biomol Struct Dyn. 2020; 39:4185-4191.

   [Crossref][Google scholar][EBSCO]

5. Abroo S, et al.Methicillin-resistant Staphylococcus aureus nasal carriage between healthy students of medical and nonmedical universities。Am J Infect Control. 2017; 45:709-712.

   [Crossref][Google scholar][EBSCO]

6. Ben Y, et al.Human health risk assessment of antibiotic resistance associated with antibiotic residues in the environment: A review。Environ Res. 2019; 169:483-493.

   [Crossref][Google scholar][EBSCO]

7. Mallah N, et al.Association of knowledge and beliefs with the misuse of antibiotics in parents: A study in Beirut (Lebanon)。PLoS One.2020; 15:e0232464.

   [Crossref][Google scholar][EBSCO]

8. Ojemaye MO, et al.Nanotechnology as a viable alternative for the removal of antimicrobial resistance determinants from discharged municipal effluents and associated watersheds: A review。J Environ Manage. 2020ss; 275:111234.

   [Crossref][Google scholar][EBSCO]

9. Kalelkar PP, et al.Biomaterial-based antimicrobial therapies for the treatment of bacterial infections。Nat Rev Mater. 2022;7:39-54.

   [Crossref][Google scholar][EBSCO]

10. Taran M, et al.Benefits and application of nanotechnology in environmental science: an overview。Biointerface Res Appl Chem. 2021;11:7860-7870.

    [Crossref][Google scholar]

11. Anselmo AC, et al.Nanoparticles in the clinic: An update。Bioeng Transl Med. 2019;4:e10143.

    [Crossref][Google scholar][EBSCO]

12. Sánchez-López E, et al。Metal-based nanoparticles as antimicrobial agents: An overview。Nanomaterials. 2020;10:292.

    [Crossref][Google scholar][EBSCO]

13. Fang M, et al.Antibacterial activities of inorganic agents on six bacteria associated with oral infections by two susceptibility tests。Int J Antimicrob Agents. 2006;27:513-517.

    [Crossref][Google scholar][EBSCO]。

14. Chen R, et al.Antibacterial activity, cytotoxicity and mechanical behavior of nano-enhanced denture base resin with different kinds of inorganic antibacterial agents。Dent Mater J. 2017;36:693-699..

    [Crossref][Google scholar]

15. Chernousova S, et al.Silver as antibacterial agent: Ion, nanoparticle, and metal。Angew Chemie - Int Ed. 2012;52:1636-1653.

    [Crossref][Google scholar][EBSCO]

16. Hamad A, et al.Silver Nanoparticles and Silver Ions as Potential Antibacterial Agents。J Inorg Organomet Polym Mater. 2020;30:4811-4828.

    [Crossref][Google scholar][EBSCO]

17. Zhang W, et al.Chemical transformation of silver nanoparticles in aquatic environments: Mechanism, morphology and toxicity。Chemosphere. 2018;191:324-334.

    [Crossref][Google scholar][EBSCO]

18. Liu J, et al.A review on bidirectional analogies between the photocatalysis and antibacterial properties of ZnO。J合金化合物。2019;783:898 - 918。

    [Crossref][Google scholar][EBSCO]

19. Jiang S, et al.ZnO Nanomaterials: Current Advancements in Antibacterial Mechanisms and Applications。Front. Chem. 2020;8.

    [Crossref][Google scholar][EBSCO]

20. Liu L, et al.Facile preparation PCL/ modified nano ZnO organic-inorganic composite and its application in antibacterial materials。J Polym Res. 2020;27.

    [Crossref][Google scholar][EBSCO]。

21. Espitia PJP, et al.Zinc Oxide Nanoparticles for Food Packaging Applications。Antimicrobial Food Packaging .

    [Crossref][Google scholar]

22. Lallo da Silva B, et al.Increased antibacterial activity of ZnO nanoparticles: Influence of size and surface modification。Colloids Surfaces B Biointerfaces. 2019;177:440-447.

    [Crossref][Google scholar][EBSCO]

23. El-Naggar ME, et al.Surface modification of SiO2 coated ZnO nanoparticles for multifunctional cotton fabrics。J Colloid Interface Sci. 2017;498:413-422.

    [Crossref][Google scholar][EBSCO]。

24. Shahriary M, et al.In situ green synthesis of Ag nanoparticles on herbal tea extract (Stachys lavandulifolia)-modified magnetic iron oxide nanoparticles as antibacterial agent and their 4-nitrophenol catalytic reduction activity。Mater Sci Eng C. 2018;90:57-66.

    [Crossref][Google scholar][EBSCO]

25. Alavi M, et al.Synthesis and modification of bio-derived antibacterial Ag and ZnO nanoparticles by plants, fungi, and bacteria。Drug Discov Today. 2021;26:1953-1962.

    [Crossref][Google scholar][EBSCO]

26. Marchese A, et al.Antibacterial and antifungal activities of thymol: A brief review of the literature。Food Chem. 2016;210:402-414.

    [Crossref][Google scholar][EBSCO]

27. Cai R, et al.Antibacterial activity and mechanism of thymol against Alicyclobacillus acidoterrestris vegetative cells and spores。LWT. 2019;105:377-384.

    [Crossref][Google scholar][EBSCO]

28. Zhu Z, et al.Microencapsulation of thymol in poly(lactide-co-glycolide) (PLGA): Physical and antibacterial properties。Materials (Basel). 2019;12:1133.

    [Crossref][Google scholar][EBSCO]

29. Shi Y, et al.Green cinnamaldehyde and thymol modified zinc oxide with double synergistic antibacterial effects in polypropylene。J Appl Polym Sci 138:

    [Crossref][Google scholar][EBSCO]

30. Emadoddin M, et al.An antifouling impedimetric sensor based on zinc oxide embedded polyvinyl alcohol nanoplatelets for wide range dopamine determination in the presence of high concentration ascorbic acid.J Pharm Biomed Anal. 2021;205:114278.

    [Crossref][Google scholar][EBSCO]

31. Jatoi AW, et al.Characterizations and application of CA/ZnO/AgNP composite nanofibers for sustained antibacterial properties。Mater Sci Eng C. 2019;105:110077.

    [Crossref][Google scholar][EBSCO]

32. Alipour N, et al.Chelating ZnO-dopamine on the surface of graphene oxide and its application as pH-responsive and antibacterial nanohybrid delivery agent for doxorubicin。Mater Sci Eng C. 2020;108:110459.

    [Crossref][Google scholar][EBSCO]

33. Wayne PA. Clinical and Laboratory Standards Institute (CLSI). Performance standards for antimicrobial susceptibility testing. INFORM SUPPL. 2011;31:100-121.

    [Google scholar]

34. Milani M, et al.Synthesis and evaluation of polymeric micelle containing piperacillin/tazobactam for enhanced antibacterial activity。Drug Deliv. 2019;26:1292-1299.

    [Crossref][Google scholar][EBSCO]

35. Tavakoli S, et al.Polydopamine coated ZnO rod-shaped nanoparticles with noticeable biocompatibility, hemostatic and antibacterial activity。Nano-Structures and Nano-Objects. 2021;25:100639.

    [Crossref][Google scholar]

36. Tavakoli S, et al.A multifunctional nanocomposite spray dressing of Kappa-carrageenan-polydopamine modified ZnO/L-glutamic acid for diabetic wounds。Mater Sci Eng C. 2020;111:110837.

    [Crossref][Google scholar][EBSCO]。

37. Norouzzadeh P, et al.Comparative study on dielectric and structural properties of undoped, Mn-doped, and Ni-doped ZnO nanoparticles by impedance spectroscopy analysis。J Mater Sci Mater Electron. 2020;31:7335-7347.

    [Crossref][Google scholar][EBSCO]

38. Abdollahi B, et al.Fabrication of ZiF-8 metal organic framework (MOFs)-based CuO-ZnO photocatalyst with enhanced solar-light-driven property for degradation of organic dyes。Arab J Chem. 2021;14:103444.

    [Crossref][Google scholar][EBSCO]

39. Nie N, et al.Direct Z-scheme PDA-modified ZnO hierarchical microspheres with enhanced photocatalytic CO2 reduction performance。Appl Surf Sci. 2018;457:1096-1102.

    [Crossref][Google scholar][EBSCO]

40. Lakshmi Prasanna V, et al.Insight into the Mechanism of Antibacterial Activity of ZnO: Surface Defects Mediated Reactive Oxygen Species even in the Dark。Langmuir. 2015;31:9155-9162.

    [Crossref][Google scholar][EBSCO]

41. Ahmed B, et al.Bacterial toxicity of biomimetic green zinc oxide nanoantibiotic: insights into ZnONP uptake and nanocolloid-bacteria interface。Toxicol Res (Camb). 2019;8:246-261.

    [Crossref][Google scholar][EBSCO]

42. Sirelkhatim A, et al.Review on zinc oxide nanoparticles: Antibacterial activity and toxicity mechanism。Nano-Micro Lett. 2015;7:219-242.

    [Crossref][Google scholar][EBSCO]

43. Morbach S, et al.Osmoregulation。Handbook of Corynebacterium Glutamicum.

    [Google scholar]